Effects of the stress state on plastic deformation and ductile failure: Experiment and numerical simulation using a newly designed tension‐shear specimen

The stress state is one of the most notable factors that dominates the initiation of ductile fracture. To examine the effects of the stress state on plasticity and ductile failure, a new tension‐shear specimen that can cover a wide range of stress triaxialities was designed. A fracture locus was constructed in the space of ductility and stress triaxiality for two typical steels based on a series of tests. It is observed that the equivalent plastic strain at failure exhibits a nonmonotonic variation with increasing the value of stress triaxiality. A simple damage model based on the ductility exhaustion concept was used to simulate the failure behaviour, and a good agreement is achieved between simulation results and experimental data. It is further shown that consideration of fracture locus covering a wide range of stress triaxialities is a key to an accurate prediction.