Dislocation Loop Formation in Nonstoichiometric (Ba,Ca)TiO 3 and BaTiO 3 Ceramics

Dislocation loops observed in nonstoichiometric and stoichiometric (Ba,Ca)TiO 3 , and in stoichiometric BaTiO 3 sintered in a reducing atmosphere, were characterized by conventional transmission electron microscopy (TEM) under two‐beam conditions and high‐resolution TEM atomic structure analysis. Dislocation loops mostly lay on {100} planes with Burgers vectors of type 〈100〉. The dynamic behavior of these dislocation loops during the electron beam irradiation (EBI), however, was classified into two different types of dislocation loops: in A‐site‐excess (Ba,Ca)TiO 3 , contrasts of dislocation loops faded completely away; in BaTiO 3 and B‐site‐excess (Ba,Ca)TiO 3 , fine‐line contrasts remained. Dislocation loops with Burgers vectors of type 1/2〈100〉 and the resultant crystallographic shear (CS) structure with a displacement vector of type 1/2〈110〉 after EBI were proposed to interpret residual line images. Disappearance of these line images in A‐site‐excess (Ba,Ca)TiO 3 strongly suggests preferential Ca ion site occupancy at the CS structure.