The surface structure of a X 12 CrNi 1810 Ti low-carbon steel after saturation with nitrogen and carbon as a consequence of electrolytic plasma nitriding and carbonitriding was studied in this work. It turned out that the X 12 CrNi 1810 Ti steel surface has a modified martensite structure and high hardness after electrolytic plasma processing. It was determined that carbide and nitride particles are formed in the surface layer during nitriding and carbonitriding followed by tempering. The X 12 CrNi 1810 Ti steel wear resistance after carbonitriding and nitriding was investigated and a decrease of the friction coefficient was observed.