Research on properties of rigid polyurethane foam with heteroaromatic and brominated benzyl polyols

Rigid polyurethane foams (RPUFs) were prepared with specific heteroaromatic and brominated benzyl polyols. The mechanical properties and thermal stability were studied using dynamic mechanical analysis (DMA) and thermogravimetric analysis (TG). The limiting oxygen index (LOI) was used to investigate the flame retardancy of the RPUFs. The results showed that the glass transition temperature (Tg) of the RPUF prepared by heteroaromatic polyol was 182°C, demonstrating an improved thermal stability for this specific heteroaromatic polyol. Brominated benzyl polyol exhibited less negative influence on mechanical properties of the RPUFs at the same time of improving the flame retardancy. The LOI values increased with an increase in the brominated polyol content to 27.5%, and the char‐forming ability of the RPUF improved; the char residue rate reached 12.6% at 700°C, but it was only 6.2% without the flame retardant. Scanning electron microscope (SEM) and energy‐dispersive spectrometry (EDS) verified that the mechanism of flame retardancy was due to a synergistic effect of the gas phase and the condensed phase.