Surfactants in heterophase polymerization: A study of film formation using force microscopy

Film formation of three different latices was studied using atomic force microscopy. The latices were made from a mixture of butyl acrylate, styrene, and acrylic acid using either a polymerizable or an unreactive anionic surfactant as an emulsifier. Sodium 11-crotonoyloxyundecan-1-ylsulfate and sodium 3-(sulfopropyl)tetradecylmaleate were used as a reactive surfactant and the unreactive surfactant was sodium dodecylsulfate (SDS). The conventional surfactant was found to migrate to the surface of the latex film to a much greater extent than did the reactive surfactants; however, also, the latter were incompletely anchored to the particle. The maleate surfactant was bound to a higher degree than was the crotonate, a finding which is in line with the relative reactivities of the two surfactants.