Electrochemical Impedance Analysis on Degradation of Commercially Available Lithium Ion Battery during Charge–Discharge Cycling

The degradation of the commercial Li ion battery was analyzed by electrochemical impedance spectroscopy, where our previous proposed equivalent circuit was applied. The degradation with the cycling was clearly explained by the main parameters of capacitive and resistive components, i.e., it responded until 300 cycles to the decrease in capacitive component, while after 300 to 550 cycles to the increase in resistive component.