The effects of addition on the electrical properties of a diffusion barrier for capacitor bottom electrodes were investigated as a function of the composition ratio of and contact size, at a temperature range of 650–800°C in air. When the Ta film was deposited without addition, it exhibited a higher total resistance and a nonohmic behavior with increasing annealing temperature, originating from the formation of a nonconductive phase by reaction between the Ta film and the external ambient oxygen after annealing. For both the and the contact system, no other phase, such as , Pt‐silicides, and Pt‐Ta compounds, was observed except for the formation of a conductive crystalline phase after annealing, followed by the prevention of surface oxidation of the diffusion barrier itself as well as the retention of the bottom electrode structure up to 800°C. This resulted in a lower total resistance and an ohmic characteristic. Therefore, it can be concluded that ohmic behavior does not depend on contact size for both contact systems and all compositions in this study.
No takes yet. Share an insight, caveat, or question.
Yoon et al. (2000) studied this question.