Effect of vinyl acetate content on the mechanical and thermal properties of ethylene vinyl acetate/MgAl layered double hydroxide nanocomposites

Ethylene vinyl acetate (EVA)/Mg‐Al layered double hydroxide (LDH) nanocomposites using EVA of different vinyl acetate contents (EVA‐18 and EVA‐45) have been prepared by solution blending method. X‐ray diffraction and transmission electron microscopic studies of nanocomposites clearly indicate the formation of exfoliated/intercalated structure for EVA‐18 and completely delaminated structure for EVA‐45. Though EVA‐18 nanocomposites do not show significant improvement in mechanical properties, EVA‐45 nanocomposites with 5 wt % DS‐LDH content results in tensile strength and elongation at break to be 25% and 7.5% higher compared to neat EVA‐45. The data from thermogravimetric analysis show that the nanocomposites of EVA‐18 and EVA‐45 have ≈10°C higher thermal decomposition temperature compared to neat EVA.