K3Na(SO4)2 : Eu nanoparticles for high dose of ionizing radiation

K 3 Na(SO 4 ) 2 : Eu nanocrystalline powder was synthesized by the chemical co-precipitation method. The x-ray diffraction pattern of the nanomaterials shows a hexagonal structure for its crystals having grain size of ∼28 nm. Transmission electron microscopy revealed that the K 3 Na(SO 4 ) 2 : Eu nanoparticles are single crystals with almost a uniform shape and size. Thermoluminescence (TL) was taken after irradiating the samples at various exposures of γ-rays from a 60 Co source. A prominent TL glow peak is observed at 423 K along with three small peaks/shoulders at around 382, 460 and 509 K. The observed TL sensitivity of the prepared nanocrystalline powder is around 4 times more than that of LiF : Mg,Ti (TLD-100) phosphor. The 423 K peak of the nanomaterial phosphor eventually shows a near linear response with exposures increasing up to very high values (as high as 70 kGy), where all the other TLD phosphors saturate. This property along with its other desired properties such as high sensitivity, relatively simple glow curve structure and low fading makes the nanocrystalline phosphor a suitable dosimeter to estimate low as well as high exposures of γ-rays. TL analysis using the glow curve deconvolution technique was also done for determining different trapping parameters.