A library of block copolymers was synthesized by varying the molecular weight of the poly(ε-caprolactone) (PCL)-diol soft segment (Mw = 850, 3050, 3700 or 7000), which was reacted with methylene diphenyl diisocyanate (MDI), 1,4-phenylene diisocyanate (PDI), 1,1′-methylenebis(4-isocyanatocyclohexane) (HMDI), or 2,4-toluene diisocyanate (TDI) with 1,4-butanediol (BD) or ethylene glycol (EG) added as chain extenders. Thermal and X-ray measurements indicated that the crystalline structure of the copolymers was largely dependent on the chain length of the PCL-diol, with no crystallization taking place with the smallest diol (Mw = 850) using MDI, TDI or HMDI. However, the copolymers produced from a PCL-diol (Mw = 850) and PDI and chain extenders (BD or EG) showed resolved crystalline peaks while no peaks appeared with other diisocyanates. Hydrolytic degradation studies demonstrated a faster degradation rate in the case of more amorphous copolymers than semi-crystalline copolymers. The cellular compatibility of the copolymers was evaluated by fabricating the entire library of polymers in a microarray format and in vitro cell culture, demonstrating that all the 57 copolymers supported cellular attachment and growth.
No takes yet. Share an insight, caveat, or question.
Khan et al. (2013) studied this question.
Synapse has enriched one closely related paper. Consider it for comparative context: