The Effect of Zr Addition on Melting Temperature, Microstructure, Recrystallization and Mechanical Properties of a Cantor High Entropy Alloy

The effect of Zr addition on the melting temperature of the CoCrFeMnNi High Entropy Alloy (HEA), known as the “Cantor’s Alloy”, is investigated, together with its microstructure, mechan-ical properties and thermo-mechanical recrystallization process. The base and Zr-modified al-loys are obtained by vacuum induction melting of mechanically pre-alloyed powders followed by recrystallization. The alloys were characterized by X-ray diffraction, scanning and transmis-sion electron microscopy, thermal analyses, mechanical spectroscopy and indentation measures. The main advantages of Zr addition are: 1) a fast vacuum induction melting (VIM) process; 2) the lower melting temperature, due to Zr eutectics formation with all the Cantor’s alloy elements; 3) the good chemical alloy homogeneity; 4) the mechanical properties improvement of recrystallized grains with a coherent structure. The crystallographic lattice of both alloys resulted to be FCC. Results demonstrate that the Zr-modified HEA presents a higher recrystallization temperature and smaller grain size after recrystallization with respect to the Cantor’s alloy, with precipita-tion of a coherent second phase which enhance the alloy hardness and strength, while maintaining a good tensile ductility.