Atomic Layer Deposition of Wet-Etch Resistant Silicon Nitride Using Di(sec-butylamino)silane and N2Plasma on Planar and 3D Substrate Topographies

The advent of three-dimensional (3D) finFET transistors and emergence of novel memory technologies place stringent requirements on the processing of silicon nitride (SiN x ) films used for a variety of applications in device manufacturing. In many cases, a low temperature (<400 °C) deposition process is desired that yields high quality SiN x films that are etch resistant and also conformal when grown on 3D substrate topographies. In this work, we developed a novel plasma-enhanced atomic layer deposition (PEALD) process for SiN x using a mono-aminosilane precursor, di( sec -butylamino)silane (DSBAS, SiH 3 N( s Bu) 2 ), and N 2 plasma. Material properties have been analyzed over a wide stage temperature range (100–500 °C) and compared with those obtained in our previous work for SiN x deposited using a bis-aminosilane precursor, bis( tert -butylamino)silane (BTBAS, SiH 2 (NH t Bu) 2 ), and N 2 plasma. Dense films (∼3.1 g/cm 3 ) with low C, O, and H contents at low substrate temperatures (<400 °C) were obtained on planar substrates for this process when compared to other processes reported in the literature. The developed process was also used for depositing SiN x films on high aspect ratio (4.5:1) 3D trench nanostructures to investigate film conformality and wet-etch resistance (in dilute hydrofluoric acid, HF/H 2 O = 1:100) relevant for state-of-the-art device architectures. Film conformality was below the desired levels of >95% and attributed to the combined role played by nitrogen plasma soft saturation, radical species recombination, and ion directionality during SiN x deposition on 3D substrates. Yet, very low wet-etch rates (WER ≤ 2 nm/min) were observed at the top, sidewall, and bottom trench regions of the most conformal film deposited at low substrate temperature (<400 °C), which confirmed that the process is applicable for depositing high quality SiN x films on both planar and 3D substrate topographies.