Plasma-Etched Pattern Transfer of Sub-10 nm Structures Using a Metal–Organic Resist and Helium Ion Beam Lithography

Field-emission devices are promising candidates to replace silicon fin field-effect transistors as next-generation nanoelectronic components. For these devices to be adopted, nanoscale field emitters with nanoscale gaps between them need to be fabricated, requiring the transfer of, for example, sub-10 nm patterns with a sub-20 nm pitch to substrates like silicon and tungsten. New resist materials must therefore be developed that exhibit the properties of sub-10 nm resolution and high dry etch resistance. A negative tone, metal–organic resist is presented here. It can be patterned to produce sub-10 nm features when exposed to helium ion beam lithography at line doses on the order of tens of picocoulombs per centimeter. The resist was used to create 5 nm wide, continuous, discrete lines spaced on a 16 nm pitch in silicon and 6 nm wide lines on an 18 nm pitch in tungsten, with line edge roughness of 3 nm. After the lithographic exposure, the resist demonstrates high resistance to silicon and tungsten dry etch conditions (SF 6 and C 4 F 8 plasma), allowing the pattern to be transferred to the underlying substrates. The resist’s etch selectivity for silicon and tungsten was measured to be 6.2:1 and 5.6:1, respectively; this allowed 3 to 4 nm thick resist films to yield structures that were 21 and 19 nm tall, respectively, while both maintained a sub-10 nm width on a sub-20 nm pitch.