Incorporation of Vanadium in Mesoporous MCM-41 and Microporous AFI Zeolites

Vanadium-containing silicate MCM-41 (V-MCM-41) zeolite and aluminophosphate AFI (VAPO-5) zeolite were synthesized and characterized by spectroscopic techniques. In as-synthesized form, the vanadyl ions (V IV O) 2+ were found to be the major vanadium species in the form of atomic dispersion on AFI by EPR and to exist simultaneously with tetrahedral ( T d ) V 5+ in MCM-41 by UV−vis. 29 Si MAS NMR investigations suggested that the vanadium ions might attach to MCM-41 through interaction with the silanol groups on the internal wall of hexagonal tubes. The V 5+ (in T d ) ions are incorporated into the lattice of MCM-41 during synthesis, while the VO 2+ (in T d ) is the loosely bound V species. The results of Raman spectroscopy indicated that the rodlike aggregation of cationic surfactant (cetyltrimethylammonium bromide, CTAB) was encapsulated in the intrachannel space of synthetic MCM-41 as in an aqueous solution. After calcination and hydration, the V 4+ species in as-synthesized V-MCM-41 was totally oxidized to +5 as shown by UV−vis and EPR spectroscopies, and they further aggregated as two-dimensional vanadate chain species that were nonuniformly deposited on the wall of MCM-41 channels as verified by Raman and HREM with EDS spectroscopies, while the V 5+ species of synthetic V-MCM-41 remains stable in a tetrahedral coordination. Comparatively, two types of VO 2+ ions were observed in as-synthesized VAPO-5 by EPR and they could be oxidized by calcination treatment. The presence of water vapor facilitates the oxidation of (V IV O) 2+ and the formation of V 2 O 5 cluster instead of isolated (V V O) 3+ species.