Nanoindentation measurements on deformation-induced α’-martensite in a metastable austenitic high-alloy CrMnNi steel

The hardness of deformation-induced α’- martensite and parent austenitic matrix in high-alloy CrMnNi steel was investigated by nanoindentation measurements inside scanning electron microscope using picoindenter. After the indentation, the microstructure was investigated by electron backscattered diffraction measurements. The hardness values for α’-martensite are only 24% higher than those of austenite. Thus, the increase in strength during the formation of deformation-induced α’-martensite is rather caused by the small grain size of α’-nuclei resulting in a dynamic Hall–Petch effect than by its “intrinsic” hardness.