SrBi 4 Ti 4 O 15 single crystals were grown, and their dielectric and ferroelectric properties were investigated along the a(b) axis and c axis, separately. The dielectric permittivity at 1 MHz was 1900 along the a(b) axis at the Curie temperature of 520 °C. This value was ten times higher than that along the c axis. With respect to the ferroelectricity, the saturated remanent polarization was 29 μC/cm2 and the saturated coercive field was 26 kV/cm along the a(b) axis under an electric field of 59 kV/cm, and ferroelectricity was not observed along the c axis.