Hydrogen in yttrium is of fundamental interest as a model system for driving metal-insulator transitions including switchable optical properties from reflecting to transparent in the visible region. We report on the structural properties of hydrogenated and deuterated thin, monocrystalline Y(0001) films grown by molecular beam epitaxy on Nb/Al₂O₃ substrates. X-ray diffraction reveals the response of the host metal lattice upon hydrogen loading. The structural coherence in all three spatial directions as well as the epitaxial relation to the substrate are maintained, though the sample undergoes structural phase transitions between the different hydride phases. With neutron reflectivity measurements we have determined the hydrogen and deuterium content since the critical angle for total reflection depends on their concentration in the sample. Measurements on hydrogenated and deuterated films show that H and D are completely interchangeable within the trihydride phase. Neutron scattering also allows us to determine the position of the deuterium atoms within the yttrium matrix. All structural information gained on thin films is in agreement with the space group P3c1 which was previously determined from powder samples.
No takes yet. Share an insight, caveat, or question.
Remhof et al. (1999) studied this question.
Synapse has enriched 3 closely related papers on similar clinical questions. Consider them for comparative context: