Top-seeding melt texture growth of single-domain superconducting pellets

The top-seeding melt texture growth (TSMTG) process is investigated in a small-vertical-thermal-gradient furnace in order to better understand the conditions for growing large single-grain pellets. An crystal was used as seed in a Y123 - Y211 composite with additions. It was shown that the role of the seed is to initiate the sympathetic nucleation growth mechanism. Indeed, the additional driving force induced by the seed is clearly demonstrated by a decrease in the undercooling of the system. The seeding crystal introduces a heterogeneous nucleation centre, leading to a very well controlled nucleation rate. Furthermore, we discuss the relation between intrinsic anisotropic growth rate and the processing rate, showing the importance of the thermal conditions of the texturing process to stabilize a sympathetic growth. By careful control of the texturing parameters, we succeeded in producing single-grain pellets as confirmed by a pole figure experiment and neutron diffraction measurements. The levitation force for pellets of 2 cm in diameter reaches 16 N when an NdFeB magnet of the same diameter is used.