Flux growth at 1230 °C of cubic Tb 2 O 3 single crystals and characterization of their optical and magnetic properties

In this work, we present the first crystal growth of cubic Tb2O3 single crystals by a controlled atmosphere flux method which uses a heavy metal free solvent working at less than half the melting temperature of this sesquioxide. Cubic millimeter-sized crystals extracted from as-grown boules are phase (powder XRD) and chemically (GDMS) pure and exhibit a Verdet constant in the visible and near-infrared spectral ranges, which is at least three times higher than that of a commercial Tb3Ga5O12 (TGG) crystal. The 1.36 mm thick crystals display a transmission coefficient higher than 77% over the 525 nm–1.38 μm spectral range. The absorption spectrum, magnetic susceptibility and specific heat measurements on the single crystals confirm the absence of detectable Tb4+ cations and other impurities.