Electromechanical properties of (1-x)Pb (Mg1/3Nb2/3)O3-xPbTiO3 (PMN-PT) single crystals with x = 0.35 were investigated as a function of different external disturbances. The polarization dependence on the electromechanical properties was first studied in order to determine the best polarization path. The correlation with X-ray measured phase ratio is presented and shows that the maximum of electromechanical properties may be correlated with a minimum rhombohedral/tetragonal phase ratio. Temperature, stress, electric field, and time (aging) stability was studied in order to determine performance-limiting factors of these materials. The rhombohedral/tetragonal phase transition is observed on temperature (80 degrees C), inducing a decrease of the electromechanical coupling factor (from 85% to 50%); but the whole properties are recovered while returning to room temperature. Stress measurement shows a large depoling of sample for stresses above 30 MPa. The PMN-PT single crystals were found to be surprisingly stable during aging, except for mechanical and dielectric losses. The same tendency was found on alternating current (AC) electric field dependence.
No takes yet. Share an insight, caveat, or question.
Sebald et al. (2004) studied this question.
Synapse has enriched 5 closely related papers on similar clinical questions. Consider them for comparative context: