Optical spectroscopy study of damage induced in 4H-SiC by swift heavy ion irradiation

Single crystals of 4H-SiC were irradiated with swift heavy ions (332 MeV Ti, 106 MeV Pb and 2.7 GeV U) in the electronic energy loss regime. The resulting damage was investigated with UV-visible optical absorption spectroscopy and micro-Raman spectroscopy. The evolution of the Raman data with fluence shows an accumulation of isolated point defects without amorphization of the material and a partial recrystallization of the structure, but only at the lowest fluence. Furthermore, the longitudinal optical phonon-plasmon coupling mode disappears upon irradiation, suggesting a strong perturbation of the electronic structure. This evolution is consistent with the optical bandgap decrease and the Urbach edge broadening that was also previously observed for the irradiation with 4 MeV Au ions.