Novel conducting fabric polymer composites as stretchable electrodes: one‐step fabrication of chemical actuators

Composite films have functioned as chemical bending actuators, where stretchable conducting fabrics were joined to both surfaces of ionomer films. This phenomenon shows that a direct metallization of either electroless or electrolytic plating having a metal dendrite formation on the ionomer film is not essential for functioning as actuators. Conducting fabric polymer composite (CFPC) actuators can be easily fabricated by a simple adhesion process using flexible conducting fabrics as electrodes. Due to their excellent contraction and expansion capabilities, gold‐ and copper‐plated knitted fabrics were employed and stably bound to Nafion‐117 film. Au‐CFPC actuators demonstrated a maximum bending displacement of ±2.5 mm at ±2 V. Cu‐CFPC gave a smaller displacement of ±0.7 mm at ±2 V, having no reverse displacement. The method described here is widely applicable, introducing conducting layers on various flexible, stretchable, and polymer substrates.