The Effect of MgO Ratio on Surface Roughness in Al-MgO Composıtes

In this study, Al-MgO reinforced metal matrix composites of 5%, 10%, and 15% reinforcement–volume ratios were produced by melt-stirring, and some mechanical properties and microstructures of composite specimens were examined. Subsequently, the produced metal matrix composites materials were machined in computer numerical control lathe by two different cutting tools, namely, carbide and coated carbide cutting tools. Machining tests were performed at the cutting speeds of 150, 200, 250, and 300 m/min, at the feed rates of 0.075, 0.15, and 0.225 mm/rev and at a constant depth of cut (1 mm). The surface roughness of machined composites was measured, and the average surface roughness (Ra) values were identified. While surface roughness value was found to decrease with increased cutting speed, it increased with the increase in feed rate. In all machining processes, the highest surface roughness values were obtained at 150 m/min cutting speed. The poorest machinability in terms of surface roughness was obtained ...