Ferroelastic Domain Switching Behaviour of [N(CH3)4]2CuCl4and [N(CH3)4]2ZnCl4Single Crystals Studied by External Stress

We studied the temperature dependence of the stress-strain hysteresis in [N(CH 3 ) 4 ] 2 CuCl 4 and [N(CH 3 ) 4 ] 2 ZnCl 4 single crystals grown by the slow evaporation method. From the obtained results, we determined that [N(CH 3 ) 4 ] 2 CuCl 4 and [N(CH 3 ) 4 ] 2 ZnCl 4 single crystals have ferroelastic characteristics in phase IV and III, and phase V and IV, respectively. Also, the ferroelastic domain switching stress due to saturation effect is approximately 0.9 MPa in [N(CH 3 ) 4 ] 2 CuCl 4 and 0.4 MPa in [N(CH 3 ) 4 ] 2 ZnCl 4 crystals. In order words, the ferroelastic phase transition due to external mechanical stress applied to these crystals causes a transformation from the twin-domain state to the single-domain state.