Experimental investigation demonstrates optimal cycling stability with six-hour ball-milled sulfur cathodes, indicating balanced particle size enhances lithium-sulfur battery performance.
Ball-milling process was applied to increase sulfur content in sulfur/polyacrylonitrile (SPAN) composites and improve electrochemical properties of Li/S batteries. In contrast to as-received PAN, pre-heated PAN was pulverized by the ball-milling, resulting in the continuous size reduction with increasing the milling time. Sulfur contents in SPAN composites synthesized with a pre-heated and milled PAN were increased with prolonging the milling time and the maximum content reached 44.5% for the milling time of 10 h. Li/S cells with SPAN electrodes delivered the first discharge capacities of 1356, 1409, 1512, and 1610 mAh/g-sulfur for milling times of 0, 1, 5, and 10 h. The 10 h-milled SPAN electrode with the highest sulfur content exhibited poor initial efficiency and low capacity retention at 100 cycles, whereas from a comprehensive viewpoint of the specific capacity and capacity retention, the 6 h-milled SPAN electrode exhibited the best electrochemical performance due to the suitable size and sulfur content.
No takes yet. Share an insight, caveat, or question.
Cho et al. (2018) studied this question.
Synapse has enriched 5 closely related papers on similar clinical questions. Consider them for comparative context: