We have designed, fabricated, and tested terahertz superconductor-insulator-superconductor (SIS) mixers having a self-compensated NbN/AlN/NbN tunnel junction and an epitaxially grown NbN/MgO/NbN microstripline. The junction as a distributed element was 0.8-/spl mu/m wide and 2.4-/spl mu/m long, and its current density was 50 kA/cm/sup 2/. The microstripline consisted of a 200-nm-thick NbN ground plane, a 180-nm-thick MgO insulator, and a 350-nm-thick NbN wiring layer. An investigation of the mixer in our receiver configuration showed flat noise characteristics from 870 to 960 GHz. The lowest receiver noise temperature of about 550 K was obtained at 909 GHz, including a 9-/spl mu/m-thick Mylar beam splitter loss and other optical losses. These characteristics suggest that SIS mixers with self-compensated NbN/AlN/NbN junctions and NbN/MgO/NbN microstriplines are appropriate for used in wideband and low-noise operations at terahertz frequencies.
No takes yet. Share an insight, caveat, or question.
Uzawa et al. (2001) studied this question.
Synapse has enriched 4 closely related papers on similar clinical questions. Consider them for comparative context: