Effect of Adding Y Elements on Microstructure Refinement and Mechanical Properties of Mg-9Al-1Zn Alloy

This is the authors' abstract. We don't add key points for this paper.

Grain refinement is of very important significance for improving the microstructure and mechanical properties of Mg alloys. This work investigated how the addition of various amounts of Y element affected the microstructure and mechanical properties of Mg-9Al-1Zn alloy. It was found that the grain size of Mg-9Al-1Zn alloy decreases as Y element content increases. When 1.2 wt.% Y element content was added, the grain size of Mg-9Al-1Zn alloy could be reduced from 334.2 μm to 134.6 μm, and grain refinement efficiency of 60% was achieved. HRTEM analysis demonstrated a good orientation relationship between the Al2Y phase and the Mg interface, and therefore, it was determined that the Al2Y phase can be used as a heterogeneous nucleation site for α-Mg grains, which promotes the grain refinement of α-Mg grain. Furthermore, the addition of Y element can also significantly refine the eutectic Mg17Al12 phase of the Mg-9Al-1Zn alloy. In this way, the mechanical properties of the Mg-9Al-1Zn alloy are significantly enhanced. It was found that the YS and UTS of the Mg-9Al-1Zn alloy reached 87 MPa and 154 MPa with the addition of 0.9 wt.% of Y element—24% and 43% higher than the Mg-9Al-1Zn alloy.