The influence of continuous stabilization on the properties of stabilized fibers and the final activated carbon fibers. Part I

This study found that, during continuous stabilization and carbonization, the shrinkage behavior of polyacrylonitrile (PAN) fibers affects the morphology and properties of the stabilized fibers, the carbon fibers, and the final activated carbon fibers. In the stabilized fibers, a higher shrinkage of the PAN fibers during the stabilization process increased the oxygen content and the core proportion and decreased the formation of ladder polymers. The effect of the shrinkage behavior of the PAN fibers on the fracture surfaces of the stabilized fibers is discussed. A microstructure model of stabilized fibers is presented, depicting fine radial structure at the fiber center. When stabilized fibers were carbonized during a continuous carbonization process, a hole structure was found in the fiber center at the temperature of 800°C, and a hollow core was found at the temperature of 1300°C. The shrinkage behaviors during the stabilization stage and the formation of the hole and the hollow core in the fiber's center during the carbonization stage are discussed. The carbon fibers developed from shrunk stabilized fibers have a lower density and lower preferred orientation than fibers developed from unshrunk stabilized fibers. But the fibers developed in this new process have greater nitrogen and oxygen content, and have a greater porosity than the traditionally‐produced fibers. The mechanical properties df the new and the traditional fibers are comparable. These characteristics are very valuable in the production of activated carbon fibers, which will be described in our next paper.