Structure and Properties of (Fe80Ga20)99.8Ce0.2 Alloy in Cast and Hot Rolled State

FeGa alloys with small additions of rare-earth elements surpass binary alloys in magnetostriction and plasticity. For this reason, they are considered promising magnetostrictive materials for various electrical engineering applications. The alloy (Fe81Ga19)99.8Ce0.2 was prepared and investigated in this work. It was found that in the cast state, it has a magnetostriction of 3/2 λ about 100 ppm, saturation magnetization of 150 emu/g, tensile strength of about 300 MPa, and fracture strain of 3%. The microstructure, crystallographic texture, and behavior when heated of the alloy were investigated. Then the ingot was subjected to forging and hot rolling with a deformation degree of 90% at 1000 °C. The structure and mechanical properties of samples cut from a hot rolling sheet were studied. Their tensile strength and fracture strain increase compared to cast state up to 600 MPa and 4% correspondingly.