Visible Light Active Photocatalytic Degradation of Bisphenol-A Using Nitrogen Doped TiO2

Nitrogen doped titania was prepared by low temperature sol-gel method using titanium precursor and nitrogen containing bases like triethylamine and tetramethyl ammonium hydroxide compounds. The materials were characterized by XRD, BET, SEM, XPS, DRS-UV, and FT-IR techniques. DRS-UV study substantially indicates shift of the absorption edge of TiO2 to lower energy region. The phase composition, crystallinity, specific surface area, and visible light activity of nitrogen doped titania depend upon the preparation conditions. Photocatalytic degradation of bisphenol-A in aqueous medium was investigated by TiO2 and nitrogen doped TiO2 under visible light irradiation in a batch photocatalytic reactor. The results indicate higher visible light activity for nitrogen doped TiO2 than commercial TiO2 (Degussa P25) for bisphenol-A degradation. The influence of various parameters such as initial concentration of bisphenol-A, catalyst loading and pH was examined for maximum degradation efficiency.