An amorphous single phase and coexistent amorphous and hcp-Mg phases in the Mg–Zn–La system were found to form in the composition ranges of 20 to 40%Zn and 0 to 12%La and 12 to 20%Zn and 0 to 4%La, respectively. The hcp phase has an ellipsoidal morphology and the particle size and interparticle distance are in the range of 5 to 10 nm and 3 to 10 nm, respectively. The mixed phase alloys exhibit high mechanical strength combined with good ductility and the tensile strength (σB) and fracture elongation (εf) at 288 K are 675 MPa and 4.3% for Mg85Zn12La3. The yield strength (σy) decreases from 570 to 150 MPa with increasing temperature from 288 to 368 K, accompanying an increase of εf to 50%. The maximum εf value is obtained near the temperature (≅365 K) at which the hcp Mg phase begins to precipitate. The largest values of σB and εf are considerably larger than those (600 MPa and 2.0%) for amorphous Mg–Zn–La alloys. The increase in σB by the formation of the mixed structure is presumably due to a dispersion hardening of the hcp supersaturated solution which has the hardness higher than that of the amorphous phase with the same composition.
No takes yet. Share an insight, caveat, or question.
Inoue et al. (1992) studied this question.
Synapse has enriched 5 related papers. Consider them for comparative context: