The impact of alkyl tri‐methyl ammonium side chains on perfluorinated ionic membranes for electrochemical applications

Three different perfluorinated type polymers as anion exchange membranes for electrochemical applications were studied. They have a sulfonamide linkage to a spacer methylene chain attached to a tri‐methyl ammonium cation, specifically using a three carbon spacer chain (PFAEM_H_C3), and methylated imide polymers with three (PFAEM_CH3_C3) and six carbon spacer chain (PFAEM_CH3_C6). There are significant number of zwitterionic side chains in the PFAEM_H_C3 polymer and very few in the PFAEM_CH3_C3 or the PFAEM_CH3_C6 polymer. They have similar halide conductivity, but the PFAEM_CH3_C6 showed highest OH− conductivity, 122 mS cm−1 at 80 °C and 95% RH. The larger spacer chain polymer, PFAEM_CH3_C6 has a higher water uptake value (λ = 9) compared to PFAEM_CH3_C3(λ = 7) at 60 °C and 95% RH in the Cl− form. Therefore, it has a larger domain spacing of 4.9 nm versus 4.1 nm from small angle X‐ray scattering data. The polymer was characterized by FTIR and DFT was used to fully assign the spectra.