Ripple structure of crystalline layers in ion-beam-induced Si wafers

Ion-beam-induced ripple formation in Si wafers was studied by two complementary surface sensitive techniques, namely atomic force microscopy (AFM) and depth-resolved x-ray grazing incidence diffraction (GID). The formation of ripple structure at high doses (~7×10¹⁷0.3em0exions∕cm²), starting from initiation at low doses (~1×10¹⁷0.3em0exions∕cm²) of ion beam, is evident from AFM, while that in the buried crystalline region below a partially crystalline top layer is evident from GID study. Such ripple structure of crystalline layers in a large area formed in the subsurface region of Si wafers is probed through a nondestructive technique. The GID technique reveals that these periodically modulated wavelike buried crystalline features become highly regular and strongly correlated as one increases the Ar ion-beam energy from 60 to 100 keV. The vertical density profile obtained from the analysis of a Vineyard profile shows that the density in the upper top part of ripples is decreased to about 15% of the crystalline density. The partially crystalline top layer at low dose transforms to a completely amorphous layer for high doses, and the top morphology was found to be conformal with the underlying crystalline ripple.