The purpose of this experiment was to prepare high-voltage porcelain ceramics as local raw materials. Density, water absorption, and volume shrinkage were determined according to the State standard (GOST 7025-91). A structural analysis was carried out using a scanning electron microscope, and an X-ray phase analysis was carried out on an Xpert PRO diffractometer. It was found, that in the initial state, ceramics consist of hexagonal (SiO2) and a small amount of monoclinic phase. Above a temperature of 1150 °С they consist of hexagonal (SiO2), an orthorhombic lattice, and also contain mullite (Al2Si2O13).