Retardation of Cs + and Cl − Diffusion Using Blended Cement Admixtures

Diffusion of cesium chloride through thin plates of hardened cement pastes was studied. Blast‐furnace slag and condensed silica fume were used as blending admixtures in an attempt to retard the diffusion of cesium and chloride ions. The curing and diffusion temperatures were varied from 27° to 60°C, and the water/solid ratio was varied from 0.30 to 0.40. Results indicate that the cesium ion diffuses more slowly than the chloride ion in hardened cement paste systems. Blending admixtures caused a further reduction in diffusivity for both ions, which is important for preventing corrosion or restricting radionuclide transport.