Electrical characterization of TiC ohmic contacts to aluminum ion implanted 4H–silicon carbide

We report on the investigation of epitaxial TiC ohmic contacts to Al ion implanted 4H–SiC. TiC ohmic contacts were formed by coevaporation of Ti and C60 at low temperature (<500 °C). A sacrificial silicon nitride (Si3N4) layer was deposited on the silicon carbide substrate prior to Al implantation in order to reach a high Al dopant concentration at the surface while maintaining a low dose. The combination of epitaxially grown TiC and the silicon nitride layer resulted in a promising scheme to make low resistivity ohmic contacts. The lowest contact resistivity (ρC) and sheet resistance (Rs) of the implanted layer at 25 °C were as low as 2×10−5 Ω cm2 and 0.6 kΩ/□, respectively.