The importance of grain boundary morphology and cohesion on intergranular strength

The morphology and constituency at grain boundaries are important in determining the properties of a poly crystalline material. In the present work it is shown that sulphur contents greater than 20 at. ppm. can embrittle nickel and nickel-base superalloys when the sulphur segregates to the grain boundaries and reduces intergranular cohesive strength. Moreover, low ductility can occur in nickel-base superalloy structures with controlled impurity levels when high stress concentrations develop in the grain boundary regions, either because of massive grain boundary shear or because of concentrated slip near grain boundaries. Résumé La morphologie et la constitution des join ts de grains sont importantes pour la détermination des propriétés de matériaux poly cristallins. Dans cette étude les auteurs montrent que des concentrations de soufre supérieures à 20 ppm. at. peuvent fragiliser le nickel et des superalliages à base de nickel quand le soufre ségrège aux joints de grains et réduit la cohésion intergranulaire. De plus, dans les superalliages à concentration contrôlée d'impuretés, une faible ductilité peut apparaître quand de fortes concentrations de contraintes se développent aux joints de grains soit sous l'effet de cisaillement massif du joint soit sous l'effet d'un glissement concentré aux joints.