Effect of supersaturation on hillock of directional Growth of KDP crystals

KDP single crystals were grown in aqueous solution by using "point seeds" with a defined crystallographic direction of 59° to the Z axis. When hillock slopes on the (100) face of KDP crystals were measured within the supersaturation (σ) range of 0 < σ ≤ 0.06, the slope of hillocks with hollow cores depended nonlinearly on supersaturation. Below σ = 0.02, the hillock slope depended on supersaturation, but when σ was ≥ 0.02, the hillock slope increased more gradually and was less dependent on supersaturation. Hollow funnel-shaped growth dislocation on the (100) face of KDP crystals was observed at σ = 0.04, characterized by large holes with micro-steps and step bunching inside, the formation of which were analyzed. The result verified that the reversed growth appears to occur within hollow channels found on growth hillocks.