A Laboratory Study of the in Situ Sulfation of Alkali Chloride Rich Deposits: Corrosion Perspective

The initial corrosive effect of small (1.35 μmol/cm 2 ) and large (13.5 μmol/cm 2 ) amounts of KCl on 304L has been investigated. The investigations were performed in both the absence and presence of 300 ppm of SO 2 at 600 °C. The results showed that in the absence of SO 2 KCl accelerates the rate of corrosion by means of two types of corrosion attack: a general attack and a steel grain boundary attack. The general attack has been proved to be initiated by K 2 CrO 4 formation. Meanwhile, the steel grain boundary attack is suggested to be accelerated by HCl released due to the chromate formation which increased with higher amounts of KCl. The presence of KCl and SO 2 resulted in the simultaneous formation of K 2 SO 4 and K 2 CrO 4 . The chromate formation resulted in a general corrosion attack. However, the oxide growth was significantly reduced due to the very fast sulfation reaction. In contrast, the steel grain boundary attack increased in the presence of SO 2 . It is suggested that the attack is accelerated by HCl released from the sulfation reaction and by sulfidation of the steel grain boundaries.