Sintering behavior of aluminum nitride powder prepared by self‐propagating high‐temperature synthesis method

Fully dense aluminum nitride (AlN) ceramics were synthesized by self‐propagating high‐temperature synthesis (SHS) method using AlN powder as raw material with Y 2 O 3 additive. The sintering behavior was studied at different sintering temperatures and additive contents. The change of phase compositions, secondary phase distributions and grain morphologies during sintering process were investigated. It is shown that fully dense ceramics using AlN powder prepared by SHS method can be obtained when the sintering temperature is above 1830 °C. Both Y 2 O 3 content and sintering temperature have an important influence on the formation of Y–Al–O phase and grain shape. When Y 2 O 3 content is identified, the grain morphology converts from polyhedron into sphere‐like shape with the rise of sintering temperature. At a certain sintering temperature, the grain size decreases with the increase in Y 2 O 3 content. The influencing mechanisms of different Y–Al–O secondary phases and sintering temperatures on the grain size and morphology were also discussed based on the experimental results.