Preparation and characterization of syndiotacticity-rich ultra-high molecular weight poly(vinyl alcohol)/imogolite blend film

To enhance the physical properties of syndiotacticity-rich (syndiotactic diad content 63·4%) ultra-high molecular weight (UHMW) (number-average degree of polymerization 12300) poly(vinyl alcohol) (PVA) film, it was solution blended with rigid-rod imogolite in dimethyl sulphoxide. In addition, the blend film prepared was stretched using a high-temperature zone drawing technique for effective orientation of the film. Through a series of experiments, it was found that imogolite caused significant changes in the structure and properties of syndiotacticity-rich UHMW PVA film, i.e. imogolite acted as an important agent which increased crystal orientation of syndiotacticity-rich UHMW PVA, resulting in enhanced tensile strength of the film. However, imogolite played a hindering role in raising the amorphous orientation of syndiotacticity-rich UHMW PVA. The maximum tensile modulus of 19·8GPa and maximum tensile strength of 1·8GPa could be obtained at the maximum draw ratio of 7·45 for PVA/imogolite blend film. In the case of PVA homo film, the highest tensile modulus and strength were 25·2GPa and 1·4GPa, respectively.