Continuous Bidirectional Deformation of an Asymmetric g‐C 3 N 4 / PLA ‐ PPC Composite Film in a Constant Solvent Environment

The frequent leakage of organic solvents necessitates the development of intelligent monitoring systems and solvent‐responsive actuators. Conventional actuators, however, often rely on “on/off” switching of external stimuli, typically resulting in passive and unidirectional deformation, which is insufficient for continuous actuation applications. This study introduces graphitic carbon nitride (g‐C 3 N 4 ), a two‐dimensional layered material, into a polylactic acid (PLA)‐poly(propylene carbonate) (PPC) system, successfully constructing an asymmetrically structured g‐C 3 N 4 /PLA‐PPC composite film. The film exhibited continuous and autonomous bidirectional deformation in a constant organic solvent environment, overcoming the limitation of unidirectional response typical of conventional materials. The bidirectional actuation performance was systematically investigated with respect to g‐C 3 N 4 content, polymer blending ratio, film geometry, and type of layered inorganic materials. The mechanism underlying the continuous bidirectional deformation of the film in a constant organic solvent environment was elucidated through systematic adsorption and structural analyses. Finally, utilizing this characteristic, biomimetic butterflies, artificial octopuses, intelligent protective devices, and smart alarms were designed, demonstrating potential application scenarios for bidirectional intelligent actuators.