Surfactant-Templated TiO2 (Anatase):  Characteristic Features of Lithium Insertion Electrochemistry in Organized Nanostructures

Thin layer electrodes (0.2−0.5 μm) of highly organized nanotextured anatase were prepared by hydrolysis of TiCl 4 in the presence of poly(alkylene oxide) block copolymer, Pluronic P-123, acting as the structure-directing agent. Electrochemical properties of these layers were studied in KCF 3 SO 3 + propylene carbonate and in LiN(CF 3 SO 2 ) 2 + ethylene carbonate + dimethoxyethane. The electrodes showed unusually fast capacitive and Li-insertion charging. A most striking effect was the occurrence of two new pairs of peaks in cyclic voltammograms in Li + containing electrolyte solutions. These, so-called S-peaks, appear in addition to the “ordinary” peaks of Li insertion into anatase. The S-peaks can act as indicators of mesoscopic ordering of the skeleton as they diminish after mechanical or thermal destruction of the organized nanotexture. We suggest that the occurrence of S-peaks is connected to the presence of amorphous TiO 2 in the organized skeleton.