The miscibility and physical and rheological properties of binary poly(vinylidene fluoride)/maleic anhydride (PVDF/MAH) blends have been systematically investigated. MAH was found to be miscible with PVDF by scanning electron microscopy (SEM), differential scanning calorimetry (DSC), and dynamic mechanical analysis (DMA). Fourier transform infrared (FTIR) investigations provided positive evidence for the specific interaction between the carbonyl groups of MAH and the methylene groups of PVDF. Rheological measurements showed that both the storage modulus and the melt viscosity of PVDF increase with the addition of MAH, followed by a decrease with excess MAH. In addition, the elongation of the PVDF/MAH blend with 10 wt % MAH is 589.7%, which is almost 5 times that of neat PVDF. It is concluded that MAH small molecules act as physical "crosslinking" points for the neighboring PVDF molecule chains due to this specific interaction between PVDF and MAH. Such a physical crosslinking function enhances the storage modulus, viscosity, and mechanical properties of PVDF.
Ye et al. (Tue,) studied this question.