Abstract With the rapid development of 5G information technology, thermal conductivity/dissipation problems of highly integrated electronic devices and electrical equipment are becoming prominent. In this work, “high-temperature solid-phase & diazonium salt decomposition” method is carried out to prepare benzidine-functionalized boron nitride ( m -BN). Subsequently, m -BN/poly( p -phenylene benzobisoxazole) nanofiber (PNF) nanocomposite paper with nacre-mimetic layered structures is prepared via sol–gel film transformation approach. The obtained m -BN/PNF nanocomposite paper with 50 wt% m -BN presents excellent thermal conductivity, incredible electrical insulation, outstanding mechanical properties and thermal stability, due to the construction of extensive hydrogen bonds and π–π interactions between m -BN and PNF, and stable nacre-mimetic layered structures. Its λ ∥ and λ ⊥ are 9.68 and 0.84 W m −1 K −1 , and the volume resistivity and breakdown strength are as high as 2.3 × 10 15 Ω cm and 324.2 kV mm −1 , respectively. Besides, it also presents extremely high tensile strength of 193.6 MPa and thermal decomposition temperature of 640 °C, showing a broad application prospect in high-end thermal management fields such as electronic devices and electrical equipment.
Tang et al. (Thu,) studied this question.