Size effects, influencing a material's strength, elongation, fatigue limit, and longevity, depend on the operative and dominant deformation and failure mechanisms. This study explores the size effects in additive manufactured (AM) GRCop-42 (Cu-4at%Cr-2at%Nb) thin wall structures fabricated via laser-powder bed fusion (L-PBF) and their impact on fatigue life. The influence of internal defects and surface topography on the fatigue life of specimens in both as-built and hot isostatic pressed (HIP) conditions across different thicknesses is investigated. Where micro-computed tomography (