Production of a sustainable cement through the usage of clay as binding element

The formulation of a calcined clay-based hydraulic binder is an innovative solution for reducing the carbon footprint in the construction industry. This binder is made from calcined clay, a natural and abundant material that does not require high-temperature firing in the 400C to 950C range. In our study, we worked respectively under the following temperatures: 550C, 650C, 750C and 850C, unlike traditional binders whose clinker is fired at a temperature of around 1450C. The blaine tests showed that the binder had been well ground, resulting in a much finer binder. We then obtained various blaines varying between 5000 and 8000 Cm2/g, unlike the blaine of the traditional binder, which is 3800 Cm2/g; the residue rate is very high compared with that of the traditional binder, due to the grinding carried out in a laboratory ball mill. The results of resistance tests at 30% gave 34.8, 48.8, 36.5 and 46 respectively; those at 40% gave 42.7, 45.4, 44.4 and 44.8, while the resistance of traditional binder gave 42.5. In other words, we obtained strengths comparable to those of the traditional binder. In addition, it was found that the manufacture of calcined clay-based hydraulic binders reduces CO2 emissions compared with traditional binders, which emit very high levels of CO2, making the production of calcined clay-based binders a more environmentally-friendly option for the cement industry. The financial assessment carried out at the end of this study shows that the production of a calcined clay-based binder is more economical than that of a traditional binder (Portland cement).