In this study, we present a new, facile, and eco-friendly approach to the synthesis of silver nanoparticles using an aqueous extract obtained from wasted goat bone, which acted as a reducing and stabilizing agent. Hydroxyapatite (GHAP) derived from the same biogenic source was then added to the Ag-NPs solution, resulting in the formation of a nanocomposite (Ag@GHAP). Biogenic GHAP and Ag@GHAP have been characterized using Fourier transform infrared spectroscopy (FTIR), dynamic light scattering (DLS), zeta potential, scanning electron microscopy (SEM), atomic force microscopy (AFM), and powder X-ray diffraction (XRD), confirming the formation of crystalline GHAP with well-dispersed silver nanoparticles. According to AFM studies, the Ag@GHAP composite exhibits a higher surface roughness alteration than GHAP. XRD revealed that the crystalline sizes of GHAP and Ag@GHAP are 10.2 and 15.6 nm, respectively. Zeta potential showed that GHAP and Ag@GHAP possessed values of −12.4 and −11.7 mV, respectively. Ag@GHAP showed a promising performance in photocatalysis and antioxidant applications as compared to GHAP. The energy band gap (Eg) values are 5.1 eV and 4.5 eV for GHAP and Ag@GHAP, respectively. Ag@GHAP showed photocatalytic activity during the degradation of methylene blue dye (5 ppm) under solar irradiation with a removal efficiency of 99.15% in 100 min at the optimum conditions. The antioxidant activity of GHAP and Ag@GHAP was determined using the DPPH method. The results showed enhanced antioxidant activity of a silver decorated sample with IC50 values of 36.83 and 2.95 mg/mL, respectively. As a result, the Ag@GHAP composite is a promising candidate in environmental treatment and scavenging of free radicals.
Alanazi et al. (Mon,) studied this question.