Using multifunctional dual-cure smart bioactive resin luting agents (DRLs) offers benefits in adhesive dentistry, but their optical stability remains a concern. Their pre-cured form is a shear-thinning structure with thixotropic gel-like behavior. The effect of their hydrophilicity and different thicknesses of nanoceramic hybrid on the final shade of milled esthetic restorations needs further investigation. This study examined how the optical function deterioration of dual-cure smart bioactive resin luting agents used to bond a CAD/CAM nano-ceramic hybrid composite would influence the restoration’s final shade at three different thicknesses. A nanoceramic hybrid composite (GD) was cut into blocks and grouped by thickness (0.8, 1.0, 1.5 mm). Ten blocks from each group were assigned to subgroups based on the DRL type: Panavia SA Universal (PN), Predicta Bioactive (PR), and ACTIVA BioACTIVE (AC). Color and whiteness changes after a 24 h/day (24 days) coffee immersion were analyzed using statistical methods (ANOVA and Tukey’s HSD for ΔE00; Welch’s ANOVA and Games-Howell for ΔWID and ΔL*). DRL type significantly affected ΔE00, ΔWID, and ΔL* (p < 0.001). All materials showed the least color change and optical function deterioration at a restoration thickness of 1.5 mm, which was below the acceptability threshold (AT). Despite PR’s bioactive functionality, it maintained its primary optical function with the least color change at GD thicknesses of 1.0 and 1.5 mm (p < 0.001). AC exhibited the greatest ΔE00 above AT, especially at a thickness of 0.8 mm (p < 0.001). ΔL*, ΔE00, and ΔWID varied significantly based on DRL type, GD thickness, and the interaction between DRL and thickness (p < 0.05). This suggests that although dual-cure smart DRLs containing bioactive glasses are advantageous, their optical function shifts may become more noticeable in thin, translucent restorations. Increasing the restoration thickness can help mitigate this by altering the optical pathway.
Yeslam et al. (Thu,) studied this question.