This study investigated high-speed air-atomized water-mist impingement cooling of 2219 aluminum alloy plates using a self-developed spray-quenching setup. Cooling intensity was controlled by varying the water loading fraction, and cooling curves were recorded using embedded thermocouples. Solution–aging treatments with conventional water quenching and mist quenching were performed, and multi-pass pre-deformation routes were applied before and/or after solution treatment. Tensile properties were evaluated at room temperature. Mist impingement cooling achieved markedly higher cooling rates than air cooling, with peak values in the order of 103 °C/s. Higher cooling intensity improved quenching efficiency and increased strength after aging. Multi-pass pre-deformation enhanced yield strength, but reduced elongation at high deformation levels, revealing a strength–ductility trade-off. These results provide guidance for optimizing quenching and pre-deformation parameters in heat treatment of 2219 aluminum alloy components.